DIP-COATING SENYAWA KALSIUM FOSFAT DARI BATU KAPUR BUKIT TUI DENGAN VARIASI RATIO MOL Ca/P MELALUI METODE SOL-GEL

Lia Anggresani

Abstract


Preparation of Dip-Coating Calcium Phosphate via sol-gel method using natural limestone Bukit Tui as calcium precursors and diammonium hydrogen phosphate as phosphorus precursors with various Ca/P mol ratio has been investigated. Etanol was used as solvent and DEA (dietanolamine) as stabilizing agent. Powder were prepared by calcinated the sol at 950oC. The results characterized by Fourier Transform Infra-red, X-Ray diffraction and Scanning Electron Microscopy. FTIR results showed that the vibration form was PO43-, P2O74-, O-H and CO2. X-Ray Diffraction (XRD) patterns of powder with various Ca/P mol ratio showed that the product of calcium phosphate was Ca2P2O7 and also found the hydroxyapatite Ca10(PO4)6(0H)2 in Ca/P ratio mol 1,7. Scanning Electron Microscopy (SEM) images of powder calcium phosphate revealed that their morphology were spheric and homogen. The coating process was done at glass substrate with coating speed 20 cm/min by calcinations at 400oC. . X-Ray Diffraction (XRD) patterns of thin layer showed that the product was Ca2P2O7 and Scanning Electron Microscopy (SEM) images of thin layer revealed that their morphology were bulk.

Key words; natural limestone, calcium phosphate, hydroxyapatite, sol-gel, dip-coating

References


Carter C. B, dan Norton M. G, 2007. Ceramic Materials, Science and Engineering, Springer Science Business Media, LLC, New York, pp 644-645.

Chong Liang, Zhaoyang Li, De’an Yang, Yuanyuan Li, Zi Yang, and William W. Lu, 2004, Synthesis of Calsium Phosphate / Calsium Sulphate Powder, J. Materials Chemistry and Physics, 88, pp 285-289.

Costa Hermes de Souza, Pereira Magalhaes Marivalda, Mansur Herman Sander, 2007, Characterization of Calsium Phosphate Coating and Zinc Incorporation on the Porous Alumina Scaffolds, Materials Research Vol 10, 1, pp : 27-29.

Dinas Energi dan Sumber Daya Mineral Provinsi Sumatera Barat. 2008. Informasi Potensi Sumber Daya Mineral dan Energi Provinsi Sumatera Barat.

Hassibi M, 1993, Factors Affecting Quality of CaO, 3rd International Sorbalyt Symposium, New Orleans, USA.

Jamarun Novesar, Harmileni dan Arief Syukri, 2010, Sintesis Senyawa Apatite Dengan Menggunakan Batu Kapur Sebagai Sumber Kalsium. Proseding Semirata PTN Barat, 1, pp 770 -777.

Kottaisamy M, Jagannathan R, Jeyagopal P, Rao R. P, dan Narayanan R. L, 1994, Eu2+ luminescence in M5(PO4)3X apatites, where M is Ca2+, Sr2+ and Ba2+, and X is F-, Cl-, Br- and OH-, J. Phys. D, 27, pp 2210 – 2215.

Liu Dean-Mo, Troczynski T, and Tseng Wenjea T, 2001, Water-based Sol-Gel Synthesis of Hydroxyapatite : Process Development, Biomaterials, 22 , pp 1721-1730.

Tkalcec E, Sauer M, Nonninger R, and Schmidt H, 2001, Sol-Gel-Derived Hydroxyapatite Powders and Coating, Journal of Materials Science, pp 5253-5263.

Utami Lisa, 2010, Pengaruh Kondisi Kalsinasi dan Penggunaan Prekursor yang Berbeda Pada Sintesis Senyawa Kalsium Fosfat Melalui Metode Pengendapan. Tesis. Padang. Universitas Andalas.

Vallet R. M, dan Gonzalez C. J. M, 2002, Calcium phosphates as substitution of bone tissues, Prog.Solid St.Chem, 32, pp 1-31.




DOI: http://dx.doi.org/10.31958/js.v7i1.123

Refbacks

  • There are currently no refbacks.


Copyright (c) 2016 Lia Anggresani

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

 

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.